查询词典 chlorhydric

Preparation of the cathode includes:shaping under the press of 40Mpa, sintering at 550℃for 1 hour and at 900℃for 8 hours and threading with molybdenum bar; Considering the literatures we choose CaCl2 as salt for preparation titanium. Pretreatment of salt is for 1 hour at 100℃and for 2 hours at 300℃. Partial pressure of oxygen which need lower than 5.11×10-7Pa to reduct titanium oxides and hygroscopic property of salt need a sealed equipment to electrolyse. And finally successfully designed a satisfied one and the results show that the equipment can be satisfied the requirment of the experiment. Flow of the inert gas is 1.5L/min, the voltage is 2.8 V, temperature is 850℃and time is 2 hours during pre-electrolysis. Flow of the inert gas is 0.2L/min, the voltage is 3.1 V, temperature is 900℃and time changes with the mass of TiO2 during electrolysis, namely the greater need the longer time; To eliminate influence of salt and other impurities, the products need to wash with distilled water and dilute chlorhydric acid , then wash with dilute hydrochloric acid under supersonic wave assistant. Finally, electrometical properties of the electrolysis of TiO2 is researched by cyclic voltammetry and chronoamperometry, and results show that there are two main reodox steps, namely from TiO2 to TiO and from TiO to Ti.

阴极制备主要包括40MPa压力下模压成型、两段式烧结(1小时内升至550℃保温1小时，再1小时升温至900℃保温8小时)及烧结后TiO2块打孔用钼棒串接三个主要环节；实验中选用CaCl2作为电解熔盐，并对其进行预处理(100℃，保温1小时； 300℃，保温2小时)；经热力学计算，还原钛氧化物的氧分压至少要低于5.11×10-7Pa，结合电解过程中所用熔盐CaCl2有极强的吸水性的特点，电解装置应有较高的密封性，自行设计了一套密封性可靠的电解装置，便于实验过程中熔盐预处理和氧分压的控制；通过干燥处理预电解过程中Ar流量大约为1.5L/min、电压为2.8 V、温度为850℃、时间为2小时，电解过程中Ar流量大约为0.2L/min、电压为3.1V、温度为900℃，实验结果表明电解时间与TiO2质量密切相关，质量越大需要电解的时间越长；通过自来水冲洗—稀盐酸浸泡、洗涤—在超声波辅助作用下稀盐酸洗涤，可减少熔盐及其它杂质对电解产物检测结果的影响；最后，通过循环伏安法、计时电流法对电解机理的研究，确定电解还原TiO2制备金属钛主要经历了TiO2-TiO-Ti的过程。

The chemistry behavior research of wollastonite indicated that the silicon-potassium fertilizer has a chemical active in organic acid.The factors affecting manurial effect of silicon-potassium fertilizer are not only soil pH and desilicification,but also content and type of organ in the soil.Wollastonite chemistry behavior indicates that silicic acid can be dissolved out from silicon-potassium fertilizer in chlorhydric acid solution if pH of solution is not smaller than 2. The drop of apparent density,increase of DBP sorptive rate and specific surface for leavings indicate that hydrated silicon oxide is polyporous,and those mineralogic feature presignify that silicon-potassium fertilizer has a role of conservation of both Moisture and Fertility and improving soil structure.After active ingredient releasing,silicon-potassium fertilizer leaves half the substance (non-active ingredient)in soil.

熟料单矿物在酸溶液中的化学行为研究表明，硅钾肥矿物在有机弱酸中的化学活性较好，影响硅钾肥肥效发挥的因素是土壤pH值和土壤的去硅化程度，还有土壤有机质的含量与种类；硅灰石在盐酸溶液中化学行为表明，在反应体系pH不小于2的情况下，硅钾肥矿物大量溶出硅酸根组分；溶解残余物表观密度降低、DBP吸着率和比表面积增加表明水合二氧化硅是以多孔形式存在，为硅钾肥具有保水保肥、改良土壤结构的提供了矿物学依据。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。