The catalyst samples were characterized by XPS and the catalytic performance of the catalyst for synthesis of lower alcohols was investigated. The XPS results indicated that the molybdenum exists as Mo6+ and (Mo6++Mo4+) in the unreduced and reduced catalyst, respectively, while the cobalt exists as Co2+ in both unreduced and reduced catalyst.

结果表明，在氧化态超细Mo-Co-K催化剂中，钼和钴分别以Mo6+和Co2+物种存在，催化剂中各物种之间存在着相互作用；随着Co/Mo比的增大，还原态催化剂中Mo4+物种的含量逐渐增大并出现极大值；催化剂上合成低碳醇反应性能与其表面的Mo4+物种有关。

6The WP/γ-Al2O3 catalyst containing 5% Ni promotor showed a higher diesel oil HDS activity than that of the corresponding sulfurized catalyst and phosphide industrial catalyst and sulfurized industrial catalyst.

含助剂Ni5%WP/γ-Al2O3催化剂柴油加氢脱硫活性最好，远高于相应无助剂硫化态催化剂以及磷化和硫化的工业催化剂。

A process for continuously preparing nm carbon tubes on fluidized bed include such steps as carrying the transition metal oxide catalyst on carrier, putting it in catalyst-activating reactor, reduction reaction by introducing the gas mixture of nitrogen gas and hydrogen or CO gas to the reactor, loading the catalyst into fluidized bed, and introducing mixed reaction gas to its to grow said nm carbon tubes on the catalyst by chemical gas-phase deposition.

本发明涉及一种流化床连续化制备碳纳米管的方法，首先将过渡金属的氧化物催化剂载于担体上，然后将其放在催化剂活化反应器内，通入流动的氢气或一氧化碳与氮气的混合气体进行还原反应，最后将催化剂送至流化床中，通入反应混合气体，流化床的下部则得到碳纳米管。本发明的方法和装置，在流化床中经过化学气相沉积，在催化剂载体上生长出碳纳米管。

According to the experimental results the reaction mechanism of gasification is proposed: firstly, the catalyst releases an oxygen atom from its rich-oxygen site to combine with a carbon atom and create a CO, then the CO molecule desorbs from the catalyst surface; next, the catalyst absorbs a CO2 molecule; and finally on the catalyst surface another CO molecule is created and the original rich-oxygen site gets an oxygen atom. On the basis of gasification process the material balance equations were built, which were solved by using numerrical integral methods and the reaction rate constants for four steps were obtained: they are 0.0703mol·g-1·min-1·kPa-1, 0.0959mol·g-1·min-1·kPa-1, 0.00539 mol·g-1·min-1 and 0.0321 mol·g-1·min-1·kPa-1 respectively.

根据实验结果推导得出了该反应过程是催化剂表面富氧活性部位先与煤焦反应生成一个CO分子，然后此CO分子从催化剂表面脱附，接着催化剂吸附气态的CO2生成一个CO并且夺得一个氧原子实现自身还原的过程，在此基础上建立了煤的催化气化的物料平衡方程组，对各步骤的反应速率常数进行了求解，在本文采用的实验条件下，各反应步骤的反应速率常数分别为0.0703 mol·g-1·min-1·kPa-1；0.0959 mol·g-1·min-1·kPa-1；0.00539 mol·g-1·min-1·kPa-1； 0.0321mol·g-1·min-1·kPa-1。

The results indicated that a dependable kinetic model could be obtained by modifying the Temkin equation by considering the H2 and NH3 adsorption factors. Activation energy for the ammonia synthesis reaction was obtained as 90.2 kJmol^(-1) after linear fitting the kinetic and thermodynamic parameters k, K(subscript H2) and K(subscript NH3) with the Arrhenius and Van't Hoff equation, which was much lower than that over iron-based catalyst, which indicated that the activation energy barrier of N2 dissociative adsorption on Ru was far lower than that on either the conventional magnetite-based catalyst or wustite-based catalyst; the hydrogen adsorption heat was 76.2 kJ mol^(-1), indicating that the adsorption of hydrogen on the Ba-Ru-K/AC catalyst was so strong that it inhibitied the dissociative adsorption of nitrogen.

结果表明，在Temkin方程中加入H2和NH3的吸附项能够获得可靠的动力学模型，用Arrhenius和Van't Hoff方程对动力学和热力学参数k、K(下标 H2)和K(下标 NH3)进行线性拟合，得到氨合成反应的活化能为90.2 kJmol^(-1)，远低于铁基催化剂，说明Ru上N2的解离吸附活化能垒远低于传统磁铁矿基催化剂和维氏体基催化剂。H2的吸附热为76.2 kJmol^(-1)，证明Ba-Ru-K/AC催化剂上H2的吸附较强烈，对N2的吸附有强烈的抑制作用。

Influence of active components in the catalyst and acetonitrile hydrogenation condition on behaviors of the catalyst and stability of the catalyst were investigated.

研究了催化剂活性组分和乙腈催化加氢工艺条件对催化剂性能的影响，并考察了该催化剂的稳定性。

The activation energy of the reaction with solid super acidic catalyst is obviously lower than that of the reaction without catalyst, Sugesting that S2O8(superscript 2-)/TiO2-Al2O3 is the the effective catalyst of the synthesis of amyl acetate.

固体超强酸S2O82-/TiO2-Al2O3使反应活化能明显降低，是乙酸异戊酯合成的有效催化剂。

Industrial gas / liquid purification catalyst, adsorbent organic compounds and metals as the main research directions, with eight experienced and deep support of the Engineering and Technology, Taiyuan, Qingdao University, Beijing Nonferrous Metal Research Institute of University established a long-term Relations of cooperation, is now a sulfur-tolerant shift catalyst, at room temperature fine desulfurizer, antichlor, sulphur recovery catalyst.

以工业气体/液体净化催化剂，吸附剂及贵金属有机化合物为主要研究方向，拥有八名经验丰富，学养深厚的高工，并于太原理工大，青岛大学，北京有色金属研究院等高校建立了长久的合作关系，现已形成耐硫变换催化剂，常温精脱硫剂，脱氯剂，硫磺回收催化剂。

In this paper, oligomerization catalyst was prepared by impregnation and the performance of Fe-Ni catalyst was studied for mixed butene oligomerization.The effect of preparation conditions, reaction conditions and molding methods of powder catalyst was separately studied on the performance of mixed-butene oligomerization.

本文采用浸渍法制备了齐聚催化剂，考察了负载型Fe-Ni催化剂在催化混合丁烯齐聚反应中的性能，研究了催化剂的制备条件、反应条件和成型等对混合丁烯齐聚性能的影响。

High-performance rare earth oxygen storage material ceria is the key material of automotive exhaust gas purification catalyst. It determines the performance and life time of the catalyst and has become the focus of competition of all countries in the field of automotive exhaust gas purification catalyst.

高性能稀土储氧材料CeO2是汽车尾气净化催化剂的关键材料，决定着催化剂的性能和寿命，是各国在汽车尾气净化催化剂领域竞争的焦点。