Results show that protons are liberated by dehydration or dehydroxylation after calcination at 500℃. These protons disrupt the silicon-oxygen-aluminium bridges where there are Al substitutions in the tetrahedral sheet of the montmorillonite. Some of silicon-oxygen and aluminum-oxygen tetrahedral invert to react with the pillaring agents and yield covalent bonds which firmly fix the pillars to the host clay. The Al-MMT are thermally and hydrothermally stable up to 700℃.

经过500℃高温焙烧后，交联剂经脱水或脱羟基释放出质子攻击蒙脱土四面体层中Si-O-Al四键，硅氧四面体和铝氧四面体发生翻转，与交联剂发生反应生成共价键，形成稳定的层柱黏土材料，在700℃高温下，Al-MMT材料不仅具有较好的热稳定性，而且具有较好的水热稳定性。

Three kinds of typical shells, such as scallop, whelk, bloody clam, as well as one kind of limestone were chosen to perform desulfurization and calcination experiments on the fluidized bed platform.The microstructures of the tested samples were mensurated by means of one mercury porosimeter.

在流化床上对3种典型贝壳---扇贝、海螺、毛蚶以及一种石灰石进行煅烧脱硫试验研究，并利用压汞仪测定试验样品的微观孔隙结构，通过最可几孔径、孔隙率、比表面积等3个结构特征参数对微观结构进行定量分析；另外，还对试验样品的化学成分进行了分析。

Through replacing copper Tri-fluoroacetate by copper α-methacrylic in Metal Organic Deposition process, the total amount of fluorine in YBCO precursor solution was reduced by about 50%. As a result, the calcination period for YBCO precurse film was dramatically reduced.

在金属有机盐沉积法制备YBCO薄膜的工艺中，采用无F的α甲基丙烯酸铜取代原来的三氟乙酸铜，可以降低前驱溶液中大约50%的氟含量。

The rodlike nano barium ferrite was prepared in the conditions of pH=4,calcination temperature at 850℃ f...

通过对几个主要参数的摸索，得出制备棒状钡铁氧体的最佳工艺条件：pH值为4，煅烧温度为850℃，煅烧时间2h。

The sagger has small expansion coefficient, high thermal stability, good thermal shock resistance, suitable for the calcination of rare earth materials, battery materials and other materials.

堇青石结合锂辉石砂锅采用人工堇青石材料为主要原料，加入少量锂辉石作为熔剂性材料生产的日用耐热砂锅，膨胀系数小，抗热震性能好，使用寿命长，可生产高档次砂锅。

The calcination and presence of adsorbed phases could lead to rearrangement of Si species in framework, and reaction of MTH aggravates desilication of the SAPO molecular sieves framework.

通过2D〓Al 3Q MAS NMR区分了多种不同配位状态的Al物种，动态跟踪了Al物种在吸附/反应过程中的变化情况。

The method is as follows: n-butyl titanate, absolute ethyl alcohol, surfactant and concentrated hydrochloric acid are fully mixed and stirred for 4 to 6 hours under room temperature to obtain precursor solution, then the precursor solution is spinningly coated on a clean conductive glass substrate of an indium oxide tin coating, and then the conductive glass spinningly coated with the precursor solution is preserved for 25 to 72 hours at the temperature of between 20 and 30 DEG C and the relative humidity of between 50 and 75 percent below, and finally undergoes a high-temperature calcination at the temperature of between 350 and 700 DEG C.

将钛酸正丁酯，无水乙醇，表面活性剂和浓盐酸充分混合，在室温下搅拌4小时-6小时得到前驱剂，然后将前驱剂旋涂在清洁的氧化铟锡镀层的导电玻璃基底上，接着在20℃-30℃，相对湿度在50％-75％下，将旋涂有前驱剂的导电玻璃保存24小时-72小时，最后经过350℃-700℃高温煅烧。

The characteristics of SO2 capture by MgO at different calcination and different sulphation temperatures have been studied experimentally.

在不同的煅烧温度和不同的硫酸盐化温度条件下，以MgO为吸收剂，进行了固硫的实验研究。

It is found that the higher the calcination temperature of MgCO3,the smaller the specific surface area of MgO is,so is the initial reaction rate of sulphation of MgO.

实验表明，菱镁矿(主要成分MgCO3)的煅烧温度越高，其煅烧产物MgO的比表面积越小，因而MgO硫酸盐化的初始反应速率越低。

Treatment at a high temperature would bring big changes to the structures of titanate nanotubes. When the calcination temperature was higher than 450℃, the tubulous structure of titanate nanotubes was destroyed and transformed into anatase phase.

高温煅烧处理对钛酸盐纳米管的结构影响较大，当温度高于450 ℃后，纳米管的层状结构被破坏，晶体结构转化为锐钛矿相的TiO2结构。

The split between the two groups can hardly be papered over.

这两个团体间的分歧难以掩饰。

This approach not only encourages a greater number of responses, but minimizes the likelihood of stale groupthink.

这种做法不仅鼓励了更多的反应，而且减少跟风的可能性。