It is easy to prepare TiO〓 nanoparticles with anatase, rutile, brookite and the mixture of anatase and rutile structures respectively through control of temperature and the ratio of /.

控制/比和反应温度可方便地制备锐钛型、金红石型、板钛矿型以及金红石型与锐钛型混合二氧化钛颗粒。

He results of TG/DTA and XRD show that Cu2+/TiO2 powder dried at 70℃ is a mixed phase of anatase and brookite. From the TEM photograph, we can find that its dispered property is good and the grains are like balls.

G/DTA和XRD分析的结果表明未经高温处理的Cu2+/TiO2粉体是锐钛矿和板钛矿的混和晶型。

The crystalline size was estimated to be around 13.3-20 nm. Raman spectra indicated there coexisted other phases and a transformation from brookite to anatase in the samples doped with 0.2% Sb.

掺入适量的Sb后，由于Sb替代了TiO2的部分Ti形成Sb-O-Ti结构，改变了TiO2的晶格结构，改善了薄膜的结晶效率，使锐钛矿结构的TiO2：Sb含量明显提高。

The minerals of Ti are ilmenite and brookite. The forms of Fe and Ti in kaolinite are absorption and structure types. The contents of them are less than 0.234% and 0.020%.

研究区高岭石晶体中铁、钛以吸附型和结构型存在，两种形式铁、钛含量分别小于0.234％和0.020％。

TiO_2 is a very important wide bandgap semiconductor, which mainly include three crystal structures. Anatase and rutile are tetragonal. Brookite is orthorhombic.

TiO_2是一种重要的宽禁带半导体材料，主要有3种晶型，即金红石、锐钛矿和板钛矿结构，其中金红石和锐钛矿属四方晶系，板钛矿属正交晶系。

When AgNO_3 concentration was higher than 0.03 M, the prepared samples consisted of anatase, brookite, rutile and metal silver nanocrystal particles, and their grain size ranges were 5-30 nm.

当AgNO_3浓度高于0.03 M时，Ag-TiO_2复合薄膜由锐钛矿、金红石、钣钛矿、金属银颗粒组成，它们的晶粒尺寸范围在5-30 nm。

1The nanocrystalline TiO2 film is prepared by sol-gel and appearance of the film is observed by SEM. The X-ray graph shows the film has lots of anatase and a few rutile TiO2, but does not have brookite TiO2. The average diameter of particle is 25nm according to Scherrer formula.

采用溶胶-凝胶法制备了纳米晶二氧化钛薄膜，通过扫描电镜观察了其形貌，X射线衍射表征显示出制备的薄膜具有大量的锐钛矿晶型和少量的金红石晶型，不含有板钛矿晶型，根据Scherrer公式计算出薄膜的晶粒的平均尺寸为25nm。

TiO2 is known to exist in three distinct structures: two tetragonal phase for anatase and rutile and a third orthornombic phase for brookite. Rutile has the most stable structure and physical and chemical properties. In rutile structure oxygen cavities move quickly so that rutile has better gas sensing respond and become a chief material use for oxygen gas sensors.

其中金红石结构是最为稳定的晶型，不但具有最为稳定的物理、化学性能，而且在金红石结构中，晶格中氧空位的迁移率较高，因而TiO_2金红石结构气敏响应效应较好，从而使金红石结构TiO_2氧化物材料成为氧敏传感器的首选材料之一。

When the is 0.1mol/l, ratio / is 0 or 4, aged at 95250℃ for 24 hours, anatase and rutile TiO〓 particles are formed respectively; when the ratio / is between 0 and 4, mixture of anatase and rutile TiO〓 particles is formed, the high the temperature the more the rutile phase. When the / is 5, aged at below 200℃ for 24 hours, amorphous product is gained, aged at 250℃ for 24 hours, olive-like TiO〓 particles with brookite structure are formed.

Ti〓=0.1mol·L〓时，95～250℃陈化，/比为0时，得到金红石型TiO〓颗粒，/比为4时，得到锐钛型TiO〓颗粒；/比介于0～4，可得到金红石型与锐钛型混合二氧化钛颗粒，温度越高含金红石型成分越多；/比为5，200℃以下陈化，得无定型产物，250℃陈化得橄榄形单分散板钛矿型二氧化钛。

Nanosized titania particles consisting of anatase, rutile and brookite phases were synthesized under solvothermal conditions with different alcohols as solvents, hexamethylene tetramine as precipitant as well as precursor of titanium trichloride.

采用不同的醇溶剂，以六亚甲基四胺为沉淀剂，以TiCl3为前驱体，通过溶剂热的方法控制合成出纳米级的锐钛矿型、金红石型和板钛矿型的二氧化钛。

This one mode pays close attention to network credence foundation of the businessman very much.

这一模式非常关注商人的网络信用基础。

Cell morphology of bacterial ghost of Pasteurella multocida was observed by scanning electron microscopy and inactivation ratio was estimated by CFU analysi.

扫描电镜观察多杀性巴氏杆菌细菌幽灵和菌落形成单位评价遗传灭活率。