A comparative study of porosity, oxide coontents, bond strength and wear resistance of 3Cr13 stainless steel coatings deposited by high velocity and regular arc spray processes was carried out. An orthogonal and rotational regression experimental method and an ordinary single-factor experimental method were adopted to evaluate the coating hardness with respect to the effect of processing parameters. The quantitative formula of processing patameters with coating hardness was obtained by means of microcomputer.The results show that, compared with the regular arc spray process, a dense?

对比研究了3Cr13不锈钢高速电弧喷涂涂层和普通电弧喷涂涂层的孔隙率、氧化物含量、涂层结合强度和滑动磨损性能，并采用多因素正交旋转回归设计和单因素对比试验的方法研究了高速电弧喷涂工艺参数对3Cr13不锈钢涂层显微硬度的影响，用微机回归得到了喷涂工艺参数与涂层硬度之间的定量关系式。

The results show that, compared with the regular arc spray process, a dense coating with lower porosity, higher bond strength and higher oxide contents were produced by a newly developed high velocity arc wire spray process.

结果表明，和普通电弧喷涂涂层相比，高速电弧喷涂涂层组织致密、孔隙率低、涂层氧化物含量增多，涂层－基体界面结合强度大于40？

Coating with lower porosity, higher bond strength and hhigher oxide?contents were produced by a newly developed high velocity arc wire spray process.The bond strength in higher than 40MPa, which is increased by 52 percent than that of regular arc sprayed coatings.

结果表明，和普通电弧喷涂涂层相比，高速电弧喷涂涂层组织致密、孔隙率低、涂层氧化物含量增多，涂层-基体界面结合强度大于40MPa，比普通电弧喷涂提高了52％。

The property of no film, micro-arc oxidation film and chromate film influenced the corrosion of joint samples which was analyzed in same corrosive conditions by calculate the corrosion effects and observe macro-photograph micro-photograph. The corrosive regularity influenced by corrosive condition factors and the corrosion resistance of different thickness of micro-arc oxidation film also be compared.

采用减重法计算连接腐蚀效应并观察试样表面的腐蚀宏观及微观形貌，对比分析了无表面处理、铬化处理及微弧氧化处理在相同盐雾腐蚀条件下对减小镁合金-钢连接腐蚀作用的差异性以及盐雾腐蚀条件参数对镁合金-钢连接腐蚀的影响规律。

During the interruptering circuit process of MCCB, two phenomena exist: electric arc back strike and arc restrike.

在塑壳断路器开断过程中存在着两种现象，电弧背后转移和过零重燃现象，这两种现象都影响着断路器的开断过程，并且都与灭弧室内电场分布有关。

For pitting surface of LY12 at different humidity in marine atmosphere, Nyquist Graph was single arc of capacitance resist and the shape of arc was identical with retractile real part.

其厚水膜高Cl-自腐蚀体系的Nyquist图是实部收缩的单一容抗弧。

Thus, the spherical-crown and saddle-shaped surfaces were demonstrated. Consequently, the basic rules and key technology of bending forming using plasma arc in practical work were obtained and the application level of the flexible forming using plasma arc had been further improved. The effects of the main parameters including power, scanning speed, scanning distance and scanning sequence had been investigated.

对成形中出现的棱角效应进行了机理分析和数值计算，结果表明棱角效应是板材沿扫描线方向受几何约束产生了较小的压应变及在扫描线上、下表面的收缩量不同所造成；提出了通过分段扫描解决棱角效应的方法，明显提高了成形质量。

When the welding current is added, on the one hand,the section of arc will more or less increase, so the fusion width will increase; on the other hand, the depth of arc crater will increase.

焊接电流增加时，一方面是电弧截面略有增加，导致熔宽增加，另一方面是电流增加促使弧坑深度增加。

The effects of arc unstable, arc characteristics and commutating circuit parameters on the process of self-excited oscillation in current commutation are discussed in detail.

理论分析和模拟计算的结果说明了不同的开断装置电弧特性和转移回路参数对自激振荡过程的作用，为高压直流断路器转移回路的参数设计提供了有效的分析和计算工具。

The morphologies and microstructures of the cathode deposits prepared by self-sustained arc discharge between graphite rods under different conditions were investigated by means of SEM and TEM,and the relationship between the morphologies and microstructures of the carbon nanotubes and the different conditions of arc discharge was obtained.

通过实现不同条件下的电弧放电，用扫描电子显微镜和透射电子显微镜对阴极沉积物中碳管的形貌和微结构进行表征，得到碳管的形貌和微结构与放电条件之间的一些对应关系。

The concept of equivalent rotationally rigidity is offered and the formula of rotationally rigidity is obtained.

主要做了如下几个方面的工作：对伸臂位于顶部的单层框架—筒体模型进行分析，提出了等效转动约束的概念和转动约束刚度的表达式。

Male cats normally do not need aftercare with the exception of the night after the anesthetic.

男猫通常不需要善后除了晚上的麻醉。