The complex decomposes activated substances with methylene, can promote formation the chemical bond between fluorine rubber and silane coupling agent; meanwhile, these activated substances can produce many kinds of amino resin containing a large number of activated function in the course of vulcanization, and improves adhesion forces with metal.

络合物分解生成具有活性亚甲基的物质，促进氟橡胶与硅烷偶联剂生成化学键，同时，这些活性物质在硫化过程中生成多种具有氮亚甲基结构特征的、含有大量活性基的氨基树脂，提高了与金属的粘接力。

The complex decomposes activated substances with methylene, can promote formation the chemicalbond between fluorine rubber and silane coupling agent; meanwhile, these activated substances canproduce many kinds of amino resin containing a large number of activated function in thecourse of vulcanization, and improves adhesion forces with metal.

络合物分解生成具有活性亚甲基的物质，促进氟橡胶与硅烷偶联剂生成化学键，同时，这些活性物质在硫化过程中生成多种具有氮亚甲基结构特征的、含有大量活性基的氨基树脂，提高了与金属的粘接力。

Given to guide the use of the word The copolymer are epoxy, with the 9M ammonia at 40 ℃ reaction 3H, on into amino resin.

利用given为引导词）该共聚物还有环氧基，与9M氨水在40℃反应3H，就转化为氨基树脂。

This paper describes the infra red spectra analysis and interpreta tion of some amino resin paints.

本文介绍了氨基树脂漆的傅立叶变换红外光谱分析及谱图解释。

The curing reaction of cationic polyacry-lates with blocked isocyanate s and amino resin was studied.

合成了阳离子型聚丙烯酸酯树脂，并分别用封闭型异氰酸酯及氨基树脂对其交联固化。

Amino resin or amino paint is mixed with a certain amount of polyisocyanate and xylene solvent etc is added.

氨基树脂或氨基漆与一定比例的多异氰酸酯固化剂混合，加入二甲苯等稀释剂不浑浊，用氨基漆与合适比例的多异氰酸酯固化剂可配成综合性能优异的双组分聚氨酯

Effects of hard/soft monomer ratio,the content of acrylic acid,the content of aromatic monomer BNMA,the ratio of amino resin curing agent to acrylic resin,the conditions of curing on properties of the films were investigated.

合成了水性丙烯酸树脂并用其配制了汽车罩光清漆，研究了硬/软单体配比、丙烯酸单体的用量、芳香酯单体的用量、氨基树脂固化剂/丙烯酸树脂的配比及固化条件对漆膜性能的影响。

Finally,ITC added with amino resin to prepare PSTU resin.The temperature、ratio and reaction time of aminition and esterification reactions were investigated.

分别考察了胺化、二异硫氰酸酯加成反应的反应温度、反应配比及反应时间等条件对树脂合成的影响，确定优化工艺条件。

The polishes for the bottle cover is prepared by the epoxy modified acrylate resin and butylated amino resin.

用环氧改性丙烯酸树脂和丁醚化氨基树脂制备瓶盖用光油。

The results indicate: With the curing temperature of the epoxy resin (E-20) and methanol etherified amino resin at 130℃ and the curing time from 15 minutes to 20 minutes, the curing product owned better curing result, higher tensile strength and best peel properties.

结果表明：环氧树脂(E-20)/甲醚化氨基树脂体系固化温度在130℃，固化时间15~20min，固化效果较好，拉伸性能较高，剥离性能最好。

For a big chunk of credit-card losses; the number of filings (and thus charge-off rates) would be rising again, whether

年美国个人破产法的一个改动使得破产登记急速下降，而后引起了信用卡大规模的亏损。

Eph. 4:23 And that you be renewed in the spirit of your mind

弗四23 而在你们心思的灵里得以更新