The results show that the grain size is refined by the addition of Nd or Dy, especially combined addition is better than single addition. With the addition of 0.2 % Nd and 0.6% Dy, the grain size is reduced from 150 μm to 60 μm. Combined addition with two rare earths elements makes the tensile strength, yield strength and elongation of ZK10 alloy increase to 191.0 MPa, 69.0 MPa, and 16.6%, increasing by 89%, 43%, 232% respectively, compared with ZK10 alloy without RE element.

结果表明：ZK10镁合金中分别加入Nd和Dy均能细化晶粒，且Nd和Dy同时加入的效果优于单一加入的效果，当同时加入质量分数为0.2% Nd和0.6% Dy时，合金的平均晶粒尺寸由原来的150 μm细化至60 μm，使ZK10合金的抗拉强度和屈服强度分别提高至191.0 MPa和69.0 MPa，伸长率达到16.6%，与未加入稀土的ZK10合金相比分别提高89%，43%和232%。

In the Ti film and the TiZr alloy film annealed at 800 ℃, there are a lot of regular hexahedron or octahedron bubbles, which are the same as the projections of equilibrium shape of their matrix crystal. With annealing temperature of 720 ℃, the bubbles in TiZr alloy annealed for 40 min are more round than those annealed for 130 min.

在800 ℃热处理后的Ti和TiZr合金中均观察到规则的六边形和八边形氦泡，对应基体材料单晶平衡外形多面体的投影。720 ℃热处理40 min后，TiZr合金膜中的氦泡比同样温度热处理130 min后的接近球形。

FL-1 type shunt is made of precision alloy board, it's copper terminals spot weled by siller alloy ensure extremely high electric capable.

FL-1 型分流器由精密合金板制成，银合金钎焊的铜端焊脚保证了接点极高的电气性能。

This invention relates to a new type nanometer crystal Fe-Zr-Nb-Si-Al-Cu series soft magnetic alloy super thin band and its process technology in which, the mother alloy is smelted by vacuum IF induction oven, an amorphous band is processed by a single quick cooling device to be processed by magnetic field heating at last to get the needed product with good soft magnet performance and iron core made by the super thin band improves its magnetic performance greatly.

本发明为一种新型纳米晶Fe-Zr-Nb-Si-Al-Cu系软磁合金超薄带及其制备工艺。由真空中频感应炉冶炼母合金，用单辊冷急装置制得非晶带，最后对非晶带进行磁场热处理，从而制得所需产品。本发明的合金超薄带具有优良的软磁性能，生产成本也较低。由本发明的超薄带制得的铁芯，其磁性能有很大改善，在国防和民用工业方面有广泛用途。

It is suitable for semi-finishing machining of soft steel, gray cast iron, Al alloy and Si+Al alloy.

适用于低碳钢、灰口铸铁、铝合金、硅铝合金的半精加工。

Ti-Ni alloy ; shape memory alloy ; spiral spring ; fatigue limit

Ti-Ni合金；形状记忆合金；螺旋弹簧；疲劳寿命

In order to enhance the anti-corrosive performance of ZK60 magnesium alloy, the chemical conversion coatings on ZK60 magnesium alloy obtained from phosphate or stannate solutions were studied.

摘 要：为了提高ZK60镁合金的耐腐蚀性能，利用磷酸盐溶液或锡酸盐溶液，考察了在ZK60镁合金上形成磷酸盐或锡酸盐化学转换膜的工艺条件及膜层的耐蚀性能。

In order to enhance the anti-corrosive performance of ZK60 magnesium alloy,the chemical conversion coating s on ZK60 magnesium alloy obtained from phosphate or stannate solutions were studied.

结果表明：在磷酸盐溶液中，当处理温度为50℃时，磷化30min后试样的电荷转移电阻为224.03Ω·cm2；当温度为80℃，反应时间为45min时，所得转换膜的Rct为377.67Ω·cm2，阻值最大，耐腐蚀性能最好；对于锡酸盐化学转化膜，90℃下，处理60min的膜层耐蚀性能最好，其Rct为388.32Ω·cm2，与磷酸盐化学转化膜相比，两种膜的保护性能相差不大。

Frame:Scott Scale Alloy 6061 butted superlight tubing D-Forged CNC machined Dropouts Delta SST bridge/Integrated Fork:Rock Shox Rebounda SL/alloy steerer .

哈哈 ------------------------------------------框架：斯科特规模6061撞上巫师超轻合金管-锻造CNC加工辍学三角洲温桥/综合叉：摇滚SHOX气柱Rebounda可溶性/合金舵手。

It adopts the International Standard of ISO and IEC standard to develop and manufacture the product of 4 series and 30 kinds, such as Alloy Aluminium and copper CCR Line, Alloy Aluminium and copper rod breakdown machine, middle wire drawing machine, fine wire drawing machine, tubular strander, specific wire drawing machine and ancillary equipment, etc.

秉承优良传统，采用ISO、IEC国际标准和国家标准研发制造产品，现已形成以铜铝合金杆生产设备系列、铜铝以及合金线拉制设备系列、绞制设备系列、特种线材加工设备等为主导产品的4大类、30余种电工专用设备。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。