The results show that proper RRA heat treatment can improve SCC properties with retention of the high strength of T6 level. After pre-aging at 100 ℃ for 24 h, retrogression at 200 ℃ for 7 min, and reaging at 100 ℃ for 24 h, the ultimate tensile strength, yield strength and elongation of the alloy are 795 MPa, 767 MPa and 9.1%, respectively. Meanwhile the failure time of the alloy applied to tensile strength of 210 MPa in 3.0%NaCl+0.5%H2O2 corrosion condition is longer than 720 h. The corresponding TEM observation shows that after retrogression for 7 min and re-aging treatment, the microstructure of grain boundary is similar to that treated in the T73 condition with coarsen and isolated distribution, and the microstructure inside grain is similar to that treated in the T6 condition with small and homogeneous distribution.

研究结果表明：在峰值时效T6状态下合金强度高，但抗应力腐蚀性能差；采用合适的RRA热处理工艺既能使合金保持T6状态下的高强度的同时，又能显著改善合金的抗应力腐蚀性能；经回归7 min RRA处理后合金的晶界类似T73态析出相聚集粗化，而晶内类似T6态析出相细小弥散分布，在拉伸应力为210 MPa和3.0%NaCl+0.5%H2O2腐蚀液中，其断裂时间大于720 h，相应的抗拉强度、屈服强度和延伸率分别为795 MPa， 767 MPa和9.1%，显示优越的综合性能。

The results show that proper RRA heat treatment can improve SCC properties with retention of the high strength of T6 level. After pre-aging at 100℃ for 24 h, retrogression at 200℃ for 7 min, and reaging at 100℃ for 24 h, the ultimate tensile strength, yield strength and elongation of the alloy are 795 MPa, 767 MPa and 9.1%, respectively. Meanwhile the failure time of the alloy applied to tensile strength of 210 MPa in 3.0%NaCl+0.5% H2O2 corrosion condition is longer than 720 h. The corresponding TEM observation shows that after retrogression for 7 min and re-aging treatment, the micro- structure of grain boundary is similar to that treated in the T73 condition with coarsen and isolated distribution, and the microstructure inside grain is similar to that treated in the T6 condition with small and homogeneous distribution.

研究结果表明：在峰值时效T6状态下合金强度高，但抗应力腐蚀性能差；采用合适的RRA热处理工艺既能使合金保持T6状态下的高强度的同时，又能显著改善合金的抗应力腐蚀性能；经回归7min RRA处理后合金的晶界类似T73态析出相聚集粗化，而晶内类似T6态析出相细小弥散分布，在拉伸应力为210 MPa和3.0%NaCl+0.5%H2O2腐蚀液中，其断裂时间大于720h，相应的抗拉强度、屈服强度和延伸率分别为795 MPa，767 MPa和9.1%，显示优越的综合性能。

The gaseous impurities in the alloys were well controlled with the sum of C, N and O less than 500wppm. For the first time it was found the strong interaction between Cr-Ti-CON, which reduces the mobility of Ti and CON, enhancing high-temperature strength and the aging-hardening property, and keeping the cold-work induced hardening at higher temperature. Aging-hardening could increase the tensile strength of V-4Cr-4Ti by 30% and could be utilized at 00 C for better economical performane of a vanadium structure. Hydrogen release will occur for the alloys tensile loaded at room temperature, which will affect the safety of a vanadium structure due to the resulting dimensional instability. For hydrogen embrittlement, impact toughness and fracture toughness of the alloy showed higher sensitivity than the tensile test elongation,so the toughness should be used as a new standard for the assessment of the embrittlement. Vanadium alloys were easily oxidized in air.

合金的气体杂质含量得到有效控制，C、N、O总量低于500wppm；首次发现Cr-Ti-CON之间的强相互作用，它使Ti、CON的高温可移动性降低，提高合金的高温强度、增强时效强化特性、使冷加工强化保持到更高温度；时效强化可使V-4Cr-4Ti的强度提高30%，可在低温（00C）下应用，提高构件的经济性；室温下，钒合金在拉应力的作用下，存在着氢释放，带来部件使用中的尺寸不稳定性，影响构件安全；氢脆是钒合金聚变应用的一个关键问题，合金的冲击韧性和断裂韧性表现出比拉伸延伸率更强的氢脆敏感性，应作为评价合金氢脆行为的新标准。

But non-religious people, when confronted with the utter lack of defensibility of all the arguments against curing aging, will often retreat to the position that, OK, they should help the effort to cure aging as soon as possible, but they don't feel like it, sorry.

但是，非宗教界的人们，当面临所有的反对治愈老化的争议完全过不了关时，他们常常会退回到他们应当努力尽快治愈老化的位置，这很好，但是，他们感到不是滋味，这很遗憾。

Second, environmental test equipment: ventilation-type aging test machine, programmable temperature and humidity chamber, temperature chamber, Thermal Shock Test Chamber, ozone aging box, UV light weathering tester, salt spray testing machine, get wet in the rain chamber, xenon lamp weather-resistant test machine, sand and dust test chamber, the standard light source box test equipment such as environmental protection.

二、环境试验设备：换气式老化试验机、可程式恒温恒湿试验箱、高温试验箱、冷热冲击试验箱、臭氧老化箱、紫外灯耐候试验机、盐水喷雾试验机、淋雨试验箱、氙灯耐气候试验机、砂尘试验箱、标准光源箱等各种环保试验设备。

National free service hotline:400 880 2959 Salt Spray test chamber\ sulfur dioxide test chamber\ High temperature test chamber\ Low temperature test chamber\High and low temperature test chamber\ High and low temperature-humidity test chamber\ High and low temperature alternating temperature humidity test chamber\ Desktop constant temperature and humidity test chamber\ Constant temperature and humidity test chamber\ Precise drying test chamber\ Vacuum drying chamber\ High and low temperature shock test chamber\ Ultraviolet accelerated weatherometer\ Xeon lamp weather resistance test chamber\ Air ventilation climatic chamber\0zone climatic chamber\ Rustproof grease humidity test chamber\ Sand and dust test chamber\ Box rain test chamber\ Pipe rain test device\ Drip box\ Alternating mould test chamber\ Salt-mist corrosion laboratory\ Salt-mist corrosion laboratory\ Large high and low temperature stepping into laboratory\ Temperature aging room\ Vacuum UV aging test chamber\ Mechanical drop test bed\ Computer control vibrating table\ Temperature and humidity and vibrating combined testing machine\ Instantaneous temperature test chamber

全国免费服务热线：400 880 2959主营产品：盐雾腐蚀试验箱/二氧化硫试验箱/高温试验箱/低温试验箱/高低温试验箱/高低温湿热试验箱。/高低温交变湿热试验箱/台式恒温恒湿试验箱/恒温恒湿试验箱/精密干燥试验箱/真空干燥箱/高低温冲击试验箱/紫外光加速老化试验机/氙灯耐气候试验箱/换气式老化试验箱/臭氧老化试验箱/防锈油脂湿热试验箱/砂尘试验箱/箱式淋雨试验箱/摆管淋雨试验装置/滴水试验装置/霉菌交变试验箱/盐雾腐蚀试验室/大型高低温步入试验室/恒温恒湿试验室/盐雾恒温恒湿高温复合试验箱/温度老化室/真空紫外老化试验箱/机械式跌落试验台/电脑控制振动台/温湿度振动三综合试验机/温度快速变化试验箱

The principle of assembly: as the climate changing and aging, human endermic collagen and VA, VB, VE, VC and free amino acid factor are in the progressive loss, causing the loss of elasticity of skin, chap skin, result in early aging and more wrinkles.

随着气候和年龄的变化，人体皮下胶原蛋白及VA、VB、VE、VC，氨基酸自由因子在逐步流失，造成人体皮肤失去弹性、干裂，提早衰老，皱纹增多。

Agricultural feminization and aging essentially indicate feminization and aging on farm labors which are the core productive element.

农业女性化和老龄化实质上是生产力要素中的核心要素－劳动者的女性化和老龄化。

Objective By using the D-galactose-induced aging mice,the effects and mechanism of Ginkgo flavone on aging were investigated.

目的 研究银杏黄酮对D-半乳糖所致小鼠学习记忆能力下降和各项衰老指标的对抗作用，以期探讨银杏黄酮的抗衰老作用机制。

Aging always has a negative effect on formability and, when aging leads to the redevelopment of an upper yield point, can result in renewed susceptibility to fluting.

在可铸性方面，老化反应总是会起到负面作用，当老化足以重新恢复较高的屈服点时，将会引起磁化系数更新，形成凹槽。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。