- 更多网络例句与黄渣相关的网络例句 [注:此内容来源于网络,仅供参考]
-
Slag test indicates that andalusite has no obvious effect on penetration. Slag penetrates along boundaries of bauxite or mullite. Al2O3 from bauxite dissolves into slag to form CA6, anorthite, gehlenite and other low melting phases which precipitate during cooling.
渣蚀试验表明,红柱石时侵蚀无明显影响,熟料液相沿莫来石和矾土骨料晶界向内渗透,氧化铝逐渐浓解与液相、渣中的氧化钙形成CA5和钙长石、黄长石等低熔相,在冷却过程中,钙长石和黄长石从液相中析出。
-
It is feasible to produce yellow chrome by using the leachate of chrome slag.
由铬渣中提取的六价铬的方法和试验的影响条件,通过研究证明了利用铬渣淋滤液制取铬黄颜料的可行性。
-
The residual Pb2+ can be removed by phosphorite to avoid bringing new pollution.(3) It is feasible to produce yellow chrome by using the leachate of chrome slag.
由铬渣中提取的六价铬的方法和试验的影响条件,通过研究证明了利用铬渣淋滤液制取铬黄颜料的可行性。
-
The results show that when the mass ratio of sodium jarosite residue to anthracite is 5∶1, reduction roast lasts at 800℃for 0.5 h, leaching is carried out at 70℃for 40 min by 0. 5 mol/L H2SO4 with liquid-solid ratio of 7∶1, 93% of both iron and nickel can be leached out.
研究结果表明:当黄钠铁矾渣与无烟煤按质量比为5∶1均匀混合,在800℃还原焙烧0.5 h,焙烧渣用0.5 mol/L硫酸溶液按液固比7∶1在70℃浸出40 min时,渣中93%的铁和镍进入浸出液中。
-
The results show that when the mass ratio of sodium jarosite residue to anthracite is 5:1, reduction roast lasts at 800℃ for 0.5 h, leaching is carried out at 70℃ for 40 mm by 0.5 mol/L H2SO4 with liquid-solid ratio of 7:1, 93% of both iron and nickel can be leached out.
研究结果表明:当黄钠铁矶渣与无烟煤按质量比为5:1均匀混合,在800℃还原焙烧0.5h,焙烧渣用0.5mol/L硫酸溶液按液固比7:1在70℃浸出40min时,渣中93%的铁和镍进入浸出液中。
-
Jarosite process can obtain high recovery rate of zinc,simultaneously,most of indium remains in the jarosite residues and a little part of indium remains in the high acidities leaching residues.
某锌精矿中铟含量很高,采用黄钾铁矾法处理该高铟锌精矿,在得到较高锌回收率的同时,大部分的铟进入矾渣,少部分进入高浸渣,从矾渣和高浸渣中可回收得到电铟。
-
Study on Improvement of Recovery of Gold and Silver from the Copper Dross Smelting in Reverberatory Furnace;2. After that, the copper in leach liquor can be extracted with the ternary extractant mainly containing P204, and the gold and silver in leach residue can be recovered by a process of cyanidation-replacement of Z.
为避免硫酸烧渣对环境的污染,以硫酸烧渣为原料,通过添加活性还原剂,用废硫酸直接还原浸出铁并制铁黄,而后用以P2 0 4为主体的三元萃取剂萃取回收浸液中的铜,用全泥氰化和锌粉置换工艺从浸渣中提取金银,较经济有效地回收利用了烧渣中的有价金属,铁、铜和金的回收率分别达到了 93。
-
The results showed that:①the crystalline phases are mainly the cuspidine, wollastonite and gehlenite with nepheline, fluorite and olivine also found in some samples under the experimental conditions;②with the bacisity and CaF_2 content increased, crystalline proportion of mold flux rises .
熔融保护渣在MoSi2高温电阻炉内以2℃/min降温速率冷却至室温,制成薄片,采用岩相显微镜分析保护渣的结晶矿相·结果表明:在本实验条件下,结晶矿相主要有枪晶石,硅灰石,黄长石,个别渣样有霞石,萤石,橄榄石;增大保护渣碱度,能促进保护渣结晶;随着渣中CaF2,Na2O,K2O和Li2O质量分数的增大,保护渣结晶化率增大;随着渣中Al2O3,MgO,BaO和MnO质量分数的增大,保护渣结晶化率减小
-
In the condition of keeping F、 K、Na content fixed, To improve slag structure and raise slag melting point and viscosity, MgO content is raised and TiO〓 is added. the main content is as follows:(1) Keeping CaO/SiO〓 fixed, MgO content rises from 10% to 16%, the free running temperature goes up 106℃, the viscosity goe down at bigger than 1425℃, but difference is little; keeping /SiO〓 fixed, MgO content rises from 10% to 16%, the free running temperature rises 87℃, the viscosity rises too; adding TiO〓 to 5%, the free running temperature goes up 98℃, the viscosity rise a little.(2) Powder crystal x ray diffraction and microscopic analysis shows: increasing MgO content, the cuspidine will decreace or even disappear, the monticellite goes up with MgO content rising, keeping /SiO〓 fixed, Akermanite content goes up, for high melting point minerals appear or go up, the free running temperature of the slag bearing F is raised; Adding TiO〓, high melting point mineral—Perovskite forms, it can making other minerals'crystalling fast, it is the reason that TiO〓 raises the free running temperature of the slag bearing F.
2对测定粘度的冷凝渣所进行的X粉晶衍射及显微分析和鉴定表明,增加MgO含量,渣中枪晶石将减少甚至消失,而钙镁橄榄石则随MgO含量增加而增加,在/SiO〓不变时,黄长石含量也有所增加,高熔点矿物的出现和增加,提高了含氟熔渣的熔化性温度;加入TiO〓熔渣中将形成高熔点矿物-钙钛矿,钙钛矿的形成还促使黄长石的结晶,这是TiO〓提高含氟熔渣熔化性温度的根本原因。
-
And then, synthesizing of middle chrome, light chrome and lemon chrome through the reaction of leachate with Pb(CH3COO)2 and Pb(NO3)2 were studied respectively.
将铬渣淋滤液与乙酸铅和硝酸铅进行反应,分别进行了中铬黄、浅铬黄和柠檬铬黄的生成试验,研究了滤液中六价铬浓度和铅盐的用量对铬黄生成反应的影响。
- 更多网络解释与黄渣相关的网络解释 [注:此内容来源于网络,仅供参考]
-
pyritic cinders:黄铁矿渣
pyritic ashes 黄铁矿粉 | pyritic cinders 黄铁矿渣 | pyroceram 耐高温玻璃
-
Marc:果渣
Mangosteen 山竹 | Marc 果渣 | Melon 黄香瓜
-
speedy:快的/迅速的/敏捷的/讯/迅速
speedway /快车道/ | speedy /快的/迅速的/敏捷的/讯/迅速/ | speiss /黄渣/
-
speiss:黄渣
speise 黄渣 | speiss 黄渣 | spelebiology 洞穴生物学
-
yellow pine:黄松
多膛炉焙烧-电炉熔炼-转炉吹炼 美国黄松(Yellow Pine)选冶厂处理锑金精矿采用的方法. 精矿在直径6.5m的十层多膛炉中焙烧,炉的前五层温度为723~743K,然后逐层升高,第十层达到823K,75%的锑以Sb2O4形态残留于烧渣中. 烧渣再在电炉内熔炼成粗锑.
-
spelaeology:洞穴学
speiss /黄渣/ | spelaeology /洞穴学/ | speleochronology /洞穴年代测定/