- 更多网络例句与纤维水镁石相关的网络例句 [注：此内容来源于网络，仅供参考]
-
From the experimental investigation,there come to a conclusion that heat insulating material of fibre brucite,which has good performance indexs,could substitute for amianthus as heat insulating material,and it will ha...
从制得的绝热材料制品的指标得出结论：纤维水镁石绝热保温材料各项指标良好。纤维水镁石绝热材料有替代石棉，制成其它绝热材料制品很好的前景。
-
In this text, we designed the testing program of fibrous brucite concrete, investigated its mechanics performance.
在本文的试验部分，我们设计了水镁石纤维混凝土的试验方案，考察了水镁石纤维混凝土的力学性能。
-
Through a large number of experiments, we have studied the interface performance of Fibrous brucite reinforced concrete / cement.
通过大量的实验，研究了水镁石纤维混凝土/水泥的界面性能。
-
The brucite fiber possesses specia1 application fields and potential new usage, which should be listed in the independent mineral ...
我国纤维水镁石矿床是一种新的矿床类型，具有独特的应用领域和潜在的新用途，应列为我国独立的矿产资源种类。
-
To the current situation of the development of the fibrous concrete at present, this text fully consulted the domestic and international documents, on the basis of forefathers' study, found a kind of natural mineral fiber, fibrous brucite. Its existence is steady in the nature. It's the ideal substitute of asbestos fibre.
针对目前纤维混凝土的发展现状，本文在充分查阅了国内外的文献资料，在前人研究的基础上，找到一种天然矿物纤维水镁石纤维，我们发现它稳定的存在于自然界中，是石棉纤维理想的替代品。
-
When it is used in the concrete reinforcement, the dispersed brucite fibers can play a better role in improving the concrete flexural strengths.
将水镁石纤维应用于混凝土，抗折强度随纤维叩解度的增加而提高，说明纤维的化学分散有利于纤维对混凝土增强作用的发挥。
-
Fibrous brucite may release free radicals in water, display chemical activity in acid solution and has cytotoxicity in body liquid.
纤维水镁石在水中可放出自由基，其在酸性环境中呈现化学活性，在体液环境中有细胞毒性。
-
After investigating physics and chemical property of fibrous brucite, it was added into cement mortar to mix. After its mechanics test, shear strength improved obviously.
本文在考察了水镁石纤维的物理和化学性能后，将水镁石纤维掺加到水泥砂浆中，测试其力学性能，抗折性能提高明显。
-
CFS is developed by using Polysulfonamide, cellulose, sepiolite andbrucite fibers as reinforced fibers, using acrylonitrile-butadiene and natural rubberas binders, using calcium carbonate, hydrated magnesium silicate, bolus alba asfiller and agent. This new material's main performances reach or are close to thesimilar products of foreign countries, and fill in the domestic gapes in the field.
首次选用有机芳砜纶纤维、纤维素纤维和无机海泡石纤维、水镁石纤维等为代石棉纤维，以丁腈橡胶和天然橡胶为弹性粘结剂，并加入碳酸钙、滑石粉、高岭土等无机填料和其它配合剂，采用压缩成张工艺成功地研制出具有工业应用价值的CFS，其主要性能指标达到或接近国外同类产品的水平，填补了国内在这一领域的空白。
-
According the analyse of orthogonal experiment content of fiber brucite and ratio of water/plaster will affect plaster mould"s most wetness break intension markedness and content of fiber brucite is mostly complication while ratio of water/plaster is subordination complication ;In the precondition of better fluidity , plaster mould"s most wetness break intension is on that content of fiber brucite is 3.6% ratio of water/plaster is 0.65,it become 2.96 Mpa which is increase 54.17% to no fiber brucite plaster moulds
根据正交实验结果，在保证石膏浆流动性的情况下水镁石纤维含量在3.6％，水膏比在0.65时标准石膏模型湿态抗折强度最大，达到2.96Mpa，比未添加水镁石纤维时的湿态抗折强度增加了54.17％，水镁石纤维含量在4.2％，水膏比为0.65时的干态抗折强度最大值达到6.92Mpa。
- 更多网络解释与纤维水镁石相关的网络解释 [注：此内容来源于网络，仅供参考]
-
nano meter brucite fiber：abbr. nmbf; 研究纳米水镁石纤维