The grindability of cement clinker was better than ordinary Portland cement, for example, on the same condition it took the high alite content Portland cement clinker 4.5min to grind to a specific surface area of 320m2/kg, while the o...
同时这种水泥熟料的易磨性优于普通硅酸盐水泥熟料：在相同条件下，磨细到比表面积320m2/kg时，这种熟料需要4.5min，而普通硅酸盐水泥熟料则需要8.0min。同时对该熟料进行了岩相检验分析。
-
On the basis of the comprehensive study and analysis of the literatures concerning the mechanism and properties of CCWC, the substances that can react with anhydrate or hydration products and other supplementary ingredients were selected, and variety of experiments were conducted by means of cross experimental design. The effects of chemical composition and dosage of raw materials, curing condition, and chemical admixtures on waterproofing ability were tested and analyzed.
本文在对水泥基渗透结晶型防水材料的作用机理和应用性能分析研究基础上，选择能与水泥混凝土中未水化水泥及部分水化产物反应的活性物质和其它的辅助成分，利用正交设计方法，研究不同组分对涂料防水性能的影响，并详细分析了原料化学成分、掺量及养护条件等参数的变化对涂料渗透结晶性能的影响，研制成功了一种以硅酸盐水泥为基础的水泥基渗透结晶型防水涂料—GT防水涂料。
-
As the cement includes sulphoaluminate clinker,it will an make important effect to the hydration and hardening of Portland cement when adding sulphoaluminate in clinker,such as accelerating the hydration rate of alite and belite clinker,improving the degree of hydration and the quantity of hydrates,and advancing early strength.
阿利特-硫铝酸盐水泥是一种早强性能优良的新型材料，由于在水泥熟料矿物体系中含有硫铝酸盐矿物，将对以阿利特为主导矿物的硅酸盐水泥的水化硬化产生重要影响：加速硅酸盐熟料水化，加快水化进程，促进水化产物生成量，提高早期强度。
-
In this paper, properties of composite binder and ordinary silicate cement were compared and the effect of dihydrate gypsum on properties of composite binder was emphatically studied.
采用硅酸盐水泥＋粒化高炉矿渣粉＋硅灰制成复合胶凝材料，与普通硅酸盐水泥进行性能比较研究，并重点研究了二水石膏对复合胶凝材料性能的影响。
-
It is also revealed that the refractoriness of Portland cement and alumina cement are actually at the identical level, and refractoriness of castable with low cement content of Portland cement, substitution of alumina cement, will not cause worsening of refractoriness.
研究还发现硅酸盐水泥耐火度与矾土水泥耐火度实为同一水平，低水泥耐火浇注料中硅酸盐水泥替代矾土水泥不会造成浇注料耐火度的恶化。
-
Experiment studied the possibility of substituting Portland cement for alumina cement to make low cement castable refactory. The results indicated that Portland cement may definitely substitute the alumina cement to make low cement castable with good performance, within the scope of low cement content of the modern low cement castable system.
试验研究了硅酸盐水泥替代矾土水泥制造低水泥耐火浇注料的可能性，结果表明在低水泥掺量的现代低水泥耐火浇注料体系中，硅酸盐水泥完全可以替代矾土水泥配制性能良好的低水泥耐火浇注料。
-
Watering concrete curing time, the introduction of Portland cement, ordinary portland cement or slag cement concrete mixing shall not be less than 7d; retardation of mixed type with admixtures, the impermeability requirements, or ash cement, fly ash cement concrete mixing shall be not less than 14d; of mixing using alumina cement concrete not less than 3d.
混凝土的浇水养护时间，对采用硅酸盐水泥、普通硅酸盐水泥或矿渣硅酸盐水泥拌制的混凝土不得少于7d；对掺用缓凝型外加剂、有抗渗性要求、或用火山灰水泥、粉煤灰水泥拌制的混凝土不得少于14d；对采用矾土水泥拌制的混凝土不少于3d。
-
German study of slag Portland cement than Portland cement information than the.
德国研究矿渣硅酸盐水泥比普通硅酸盐水泥的信息比。
-
They used limestone of different quality and large-fluctuant-range waste stone in proportion and substituted a part of clay with clay stone to produce cement. And the physical performance of the produced Portland cement was improved greatly-28 d strength increased from 50.4MPa to 54.5MPa, and output of the rotary kiln increased. Moreover, the company also tried to use green shale as admixture to produce compound cement and successfully produced compound Portland cement with a little low early strength and a little higher 28d strength than slag Portland cement. And the cement cost decreased 19.59 yuan per ton.
将CaO含量波动范围较宽的废石与不同品位石灰石按比例搭配使用，将其粘土质特性的废石替代部分粘土生产；而且生产的硅酸盐水泥熟料物理性能有较大提高，28d强度由原来的50.4 MPa提高到54.5 MPa，窑产量也有一定的提高；此外，该公司还进行了将绿色页岩作混合材生产复合水泥的生产探索，成功生产出了早期强度略低，但28d强度略高于矿渣硅酸盐水泥的复合硅酸盐水泥，且使水泥生产成本降低19.59元/t。
-
The selection and control method of lime saturation factor in preparation for alite-rich Portland cement clinker was discussed.
分析了不同C3S含量硅酸盐水泥熟料的矿物形成过程、易烧性及矿相结构差异，对高C3S含量硅酸盐水泥熟料适宜的极限石灰率值选择及控制方法进行了探讨。
- 更多网络解释与硅酸盐水泥相关的网络解释 [注：此内容来源于网络，仅供参考]
-
portland cement：硅酸盐水泥
硅酸盐水泥(Portland cement) 是以硅酸钙为主要矿物组成的水泥的统称,国际上统称为波特兰水泥. 这类水泥包括不掺或掺有混合材料的各种硅酸盐水泥,中国按其混合材料的掺加情况,共分为如下五类.
-
white portland cement：白色硅酸盐水泥
用于水泥和混凝土中的粉煤灰 Fly ash used for cement and concrete | 白色硅酸盐水泥 White portland cement | 白色硅酸盐水泥白度试验方法 Test method for whiteness of white portland cement
-
portland cement concrete：硅酸盐水泥混凝土
portland cement 波特兰水泥 | portland cement clinker 波特兰水泥熟料 | portland cement concrete 硅酸盐水泥混凝土
-
sulphate-resisting Portland cement：抗硫酸盐硅酸盐水泥
3.10 快硬硅酸盐水泥 rapid hardening portland cement | 3.11 抗硫酸盐硅酸盐水泥 sulphate resisting portland cement | 3.12 白色硅酸盐水泥 white portland cement
-
Composite portland cement：复合硅酸盐水泥
用作水泥混合材料的工业废渣活性试验方法 Test method for activity of industrial was... | 复合硅酸盐水泥 Composite portland cement | 水泥水化热测定方法 (溶解热法) Test method for heat of hydration of ceme...
-
iron portland cement：铁硅酸盐水泥
iron portland cement ==> 含铁硅酸盐水泥,铁渣水泥 | iron Portland cement ==> 铁硅酸盐水泥 | iron powder ==> 铁粉
-
iron portland cement：含铁硅酸盐水泥,铁渣水泥
iron pole piece ==> 软铁极片 | iron portland cement ==> 含铁硅酸盐水泥,铁渣水泥 | iron Portland cement ==> 铁硅酸盐水泥
-
Portland blastfurnace-slag cement, portland pozzolana cementportland fly-ash cement：矿渣硅酸盐水泥、火山灰质硅酸盐水泥及粉煤灰硅酸盐水泥
水泥压蒸安定性试验方法 A... | 矿渣硅酸盐水泥、火山灰质硅酸盐水泥及粉煤灰硅酸盐水泥 Portland blastfurnace-slag cement, portland pozzolana cementportland fly-ash cement | 纤维增强塑料性能试验方法总则 The ...
-
portland slag cement：矿渣硅酸盐水泥
portland pozzolan concrete 火山灰硅酸盐水泥混凝土 | portland slag cement 矿渣硅酸盐水泥 | position 位置
-
portland slag cement：矿渣水泥 (矿渣硅酸盐水泥 )
矿化水 mineral water | 矿渣水泥 (矿渣硅酸盐水泥 ) portland-slag cement | 溃坝洪水 dam break flood