- 更多网络例句与渗氮相关的网络例句 [注：此内容来源于网络，仅供参考]
-
Time are tested under different kinds of stress for nitrided and un-nitrided specimens made from 35CrMo steel. The testing time ranges from 70 to 80 hours. The following equations are regressed from the tested curves: Un-nitrided specimens:〓 Nitrided specimens:〓 The above equations are consistent with the first stage theory for creep.
为此本文通过实验，测试了35CrMo钢渗氮和未渗氮两种试样在500℃时不同应力情况下的应变随时间的变化曲线，实验时间为70-80小时，将测得的曲线回归出以下方程：未渗氮样品：〓渗氮样品：〓以上方程符合蠕变的第一阶段陈化理论公式。
-
The small size particles produced during ferrovanadium sizing operation are formed into nitrided briquette so as to obtain nitrided ferrovanadium, The effect of ferroalloy size, pressure, nitriding temperature and nitniding time was studied on the nitrogen content of the product.
对高钒铁合金精整过程中产生的细颗粒物料进行压块渗氮，得到氮化钒铁产品，研究了合金粒度、压块压强、渗氮温度、渗氮时间对产品含氮量的影响。
-
The effect of NH 4Cl on the nitridation of intermetallic compound TiAl was investigated.
介绍了NH4 Cl对TiAl基合金渗氮的影响以及渗氮后其渗层的组织特点。
-
The results of Monte Carlo simulation disclose that in large range of nitrogen fugacity the solubility of the interstitial nitrogen in αFe obeys Sievert's law. This range is much larger than that in γFe-N system. The results also show that in order to get the same level of interstitial nitrogen solubility in αFe-N system during solid state nitride, larger nitrogen fugacity is needed at the lower temperature.
该逸度范围比面心立方结构的Fe-N体系中大得多；由模拟计算结果还可知，在固体渗氮过程中，若要使合金含有同样浓度的固溶氮，渗氮温度较低时应保持较高的氮分压。
-
In this paper,the principle of nitriding and the technology of nitrogen potential control were introduced.
简要介绍了渗氮机理及氮势控制技术，并在GN70 / 12 0型井式渗氮炉内进行了可控渗氮试验。
-
This can be done carburizing, cyaniding, nitriding, carbonitriding, induction hardening, and flame hardening.
这可以通过渗碳剂、氰化、渗氮、碳氮共渗、感应淬火、火焰淬火来完成。
-
Sulphurized-nitrided compound layer is prepared on the surface of drilling pipe joint material 35CrMo steel by the application of ion nitriding and ion sulfurizing technology.
应用离子渗氮与离子渗硫技术，在钻杆接头材料35CrMo钢表面制备了硫氮复合处理层。采用M-200环块磨损试验机，对比研究了原始渗氮表面与硫氮复合表面在干摩擦条件下的抗磨损性能。
-
The distribution of nitrogen concentration and the microstructure of the nitrided layer were measured and observed by EPMA and SEM respectively.
在氮气中对304奥氏体不锈钢进行固溶渗氮，用电子探针测定了渗氮层的氮浓度分布，用扫描电子显微镜观察了渗氮层的金相组织。
-
The nitrided layer formed on the surface of stainless steel consists of a nitrogen supersaturated austenite which is maintained to very high nitrogen concentrations and is of high hardness and good corrosion resistance.
与一般离子渗氮不同的是，这些新方法是在真空度较高、温度较低的条件下进行渗氮，可以充分地利用离子的能量提高渗氮效率。
-
The effect of the surface treatment on the fretting wear behavior of 316LVM austenitic stainless steel was investigated in the Ringer's solution by a Servo Hydraulic Dynamic Test machine.
采用液压伺服微动试验机，在模拟体液中试验研究了430℃渗氮、430℃氮碳共渗与500℃渗碳等3种表面改性工艺对医用奥氏体不锈钢316LVM微动腐蚀磨损性能的影响。
- 更多网络解释与渗氮相关的网络解释 [注：此内容来源于网络，仅供参考]
-
liquid pressure nitriding：加压液体渗氮(法)
liquid pressure drive | 液压传动 | liquid pressure nitriding | 加压液体渗氮(法) | liquid pressure recovery factor | 液体压力恢复系数
-
nitride：氮化物;硝化;渗氮
nitric acid 硝酸 | nitride 氮化物;硝化;渗氮 | nitrification (氮的)硝化作用
-
nitride：氮化物渗氮
nitridation 渗氮 | nitride 氮化物渗氮 | nitriding hardening 渗氮硬化
-
nitridation：渗氮
渗碳 carbonization | 渗氮 nitridation | 渗铬 chromizing
-
nitriding：渗氮(氮化)
vacuum carburizing 真空渗碳 | nitriding 渗氮(氮化) | tufftride 软氮化
-
ion nitriding：离子渗氮
74、气体渗氮 gas nitriding | 75、离子渗氮 ion nitriding | 76、退氮 denitriding
-
gas nitriding：气体渗氮
73、液体渗氮 liquid nitriding | 74、气体渗氮 gas nitriding | 75、离子渗氮 ion nitriding
-
azotise：渗氮;氮化处理
axle 轴;轴杆 | axle lining 轴衬 | azotise 渗氮;氮化处理
-
Nitrided Steel：渗氮钢
Nitrated Steel 氮化钢 | Nitrided Steel 渗氮钢 | Nitriding Steel 氮化钢; 氮化钢
-
nitrided case：渗氮层
氮化层 nitride layer | 渗氮层 nitrided case | 渗氮层厚度 nitrided case depth