The results show that the brush-plating coating is even and compact from section plane with good toughness and adhesion. The microhardness of the coating is 230.6HV0.5 which is 3 times of cast aluminium substrate. The wear resistance of the coating is 3 times of cast aluminium substrate. But the friction coefficient of the coating is 0.70 which is more high than that of the substrate, which is favorable for the fixed conjugate between the axis sheath and the axis seat of the gear-box.

结果表明，镀层厚度分布均匀、致密，镀层与基体界面清晰，未出现氧化物夹层，镀层的韧性和结合强度均较好；测得碱性铜及铸铝基体的显微硬度分别为230.6、74.2HV0.5；碱性铜的镀制使基体表面显微硬度及耐磨性均提高了2倍多，磨损状况明显改善。

The combination of corundum-coated cBN abrasive with vitrified bond is better than that of Ti-coated or un-coated cBN. And the buffer layer from cBN abrasive, corundum coating to bond is perfect because part of corundum coating melts into vitrified bond to build dentation combination.

表面涂覆刚玉和镀覆Ti的cBN磨粒与结合剂的结合效果均比未镀覆的好，但涂覆刚玉比镀覆Ti的效果更好，刚玉涂层以牙形溶入结合剂中使得磨粒、镀层和结合剂三者过渡良好。

At present,this apparatus is used mainly for the examination of the perfectness of convergent spherical wave surface with aperture angle≤1:3,hence it can be used for the non-contact direct test of aluminized or unaluminized concave mirrors with any ...

因此可以用来无接触的直接检验任意口径的镀铝或未镀铝的凹球面镜；加入辅助镜后可以检验平面镜、天文望远镜用的各种非球面镜、介质的均匀性、光学系统的质量、光轴校正及安装变形情况；也可给出物镜对于现用激光波长(6328)的波面差及测出某些象差。

We used ITO glass substrate and high purity（99.99%） titanium , put to use sputtering process, add to high purity O2 make it complete the best structure film and the thickness about 1400 . By way of 500℃ anneal could got a better anatase phase, this result could easy reaction with electrolyte to increase electron-transferred. Used as spin casting covering PR on ITO substrate, transferring patterns of array circular shapes on a mask to photography, used optimize temperature and time to hard bake. Finally used HCl to etching underexposed TiO2 area, and acetone to tripper top PR, make it to accomplish pillars shape TiO2 electrode.

本研究使用ITO玻璃基板为底材在以高纯度钛(99.99%)为靶材，利用溅镀方式通入纯氧使其行成高纯度TiO2镀於ITO基板上行成厚度约1400的薄膜，且经500℃高温烧结使其行成最强的锐钛矿结晶相，此晶相有利於与电解液反应进而增加电子的转移，提升太阳能电池最佳的效率，在以旋转涂布方式铺上光阻，以矩阵排列的圆孔光罩曝光、最佳的温度及时间来烘烤、显影后；使用盐酸以等向性湿蚀刻方式蚀刻未曝光之TiO2区域，最后利用鈵铜将最上层光阻去除，使其行成柱状TiO2的电极。

The b usiness proposal is b usiness secret, thereinto except the publicized data and materials, the reference and use of all the referred unpublicized contents and data are limited, and it only for allowable addressees of our company.

线路将要么以单圈3 段3金属丝线路要么以单段2金属丝线路的规格建设。线路应由未接地的木头和镀锌的钢柱组成。

Chrome paper, cardboards, table tissues, coated or uncoated paper; PP non-woven; corona treated, 38-40dyn/cm alclad paper, PE, OPP film.

铜版纸、卡纸、餐巾纸、涂布或未涂布的纸张印刷；无纺布材料；经电晕处理后印刷表面张力达到38-40dyn/cm的镀铝纸、PE、OPP塑料薄膜。

In our experimental results, we have transferred the GaAs solar cells from GaAs substrates onto the mirror-coated copper substrates with the base layer thickness of 1.5 μm. The photovoltaic performance of the orginal GaAs solar cell on a GaAs substrate was also measured. Under AM1.5G and without anti-reflective coatings conditions, it is found that the Jsc can increase from 12.6 mA/cm2 to 13.82 mA/cm2, while the conversion efficiency can improve from 7.91% to 8.53%. As a result, the enhanced Jsc and η data of the GaAs solar cells can be contributed by the AuGe/Au mirror between the GaAs solar cell and copper substrate.

在实验验证方面，本实验室将砷化镓太阳电池由砷化镓基板转移至铜基板上，在基极厚度1.5 μm、AM 1.5G、以及元件未披覆抗反射膜的条件下，短路电流密度可由12.6 mA/cm2提升至13.82 mA/cm2，增加9.7%，而转换效率则可由7.91%提升为8.53%，这结果显示当砷化镓太阳电池基极底部镀有金属反射层时，的确能适度地提升太阳电池的短路电流密度及转换效率。

Furthermore, the gate is directly sitting on the undoped layer, and it shows larger gate turn-on voltage and broad gate swing.

此外，闸极直接镀於未掺杂层，因此有大的闸极导通电压宽广的闸极电压操作范围。

Hexavalent chromium in corrosive preventive coatings of unpainted metal sheetings and fasteners used for corrosion protection and Electromagnetic Interference Shielding in equipment falling under category three of Directive 2002/96/EC (IT and telecommunications equipment).

2002/96/EC指令内三类产品的设备内用于防腐蚀和抗电磁干扰的未镀层金属板和紧固件中作为防腐蚀镀层的六价铬。

Results of experimental research on diamond surface metallization with electrolyse plating and vacuum plating show that strength, thermal stability and penetration rate of metallized diamond are much better than that of nonmetallilized diamond, and performances of diamond plated with Ti are the best among all plated diamonds.

利用化学镀和真空镀 2种方法对金刚石表面进行金属化处理的试验研究结果表明，镀膜金刚石较未镀膜金刚石的抗压强度、热稳定性等性能和碎岩效果均有很大提高，其中真空镀Ti的效果最好。

与未镀的相关的网络解释 [注：此内容来源于网络，仅供参考]

black sheet iron：黑钢皮

black sheep | 害群之马, 败家子 | black sheet iron | 黑钢皮 | black sheet | (未镀的)黑钢板, 薄钢板 黑铁皮

unfiltered：未过滤的 未滤过的

unfilmedtube 未镀铝屏电子管 | unfiltered 未过滤的 未滤过的 | unfilteredwater 未过滤水

ungainly：难看的

unfurnished /无设备的/无准备的/ | ungainly /难看的/ | ungalvanized /未镀锌的/

ungarbled：未经筛分的

;plate 未镀锌薄板;黑铁板 | ungarbled 未经筛分的 | unglazed 未上釉的;无光的

brut：原始的,未加工的

bourrelet 凸边,轮缘 | brut 原始的,未加工的 | cadmiage 镀镉

unfilmed：未敷膜的

unfilledstate 未满态 | unfilmed 未敷膜的 | unfilmedtube 未镀铝屏电子管

ungalvanized：未镀锌的

ungaite 奥长英安岩 | ungalvanized 未镀锌的 | ungalvanizedironandsteel 未镀锌钢铁

ungalvanized：未(或不)镀锌的

unfreeze 使解冻 | unfrozen 不冻的;不冷的;解冻的 | ungalvanized 未(或不)镀锌的

ungalvanized plate：未镀锌薄板;黑铁板

ungalvanized 未(或不)镀锌的 | ungalvanized plate 未镀锌薄板;黑铁板 | ungarbled 未经筛分的

unplated：无液层的;未镀过的

unpitled 带核的;未去核的 | unplated 无液层的;未镀过的 | unpleasant odor 气味不良