slag forming
- slag forming的基本解释
-
-
造渣
- 更多网络例句与slag forming相关的网络例句 [注:此内容来源于网络,仅供参考]
-
Lubrification modifier of low sulfur diesel oil;2. The slag forming process and production of low sulfur pipeline steel X52 are described.
对低硫管线钢X52的冶炼造渣工艺和实际生产情况进行阐述,讨论了进一步开发利用LF炉冶金功能问题。
-
MgO-C brick has a good erosion resistance but Al〓O〓-C brick is better. Corrosion mechanism for refractory without carbon is that FeO and oxides of molten slag take place chemical reaction with constituents of refractory and forming low fusing point compounds to be dissolved in molten slag. For those refractory containing graphite carbon is to be decarburized in advance and to form decarburizing layer and metamorphosis layer. The subsequent corrosion is decarburizing and taking chemical reaction to form low fusing point compounds and dissolved in molten slag at the same time.
铁浴中硅和钛的扩散是影响铁浴及熔渣与耐火材料作用的重要因素,耐火材料中添加的TiO〓和SiC受熔渣氧化和侵蚀,将被部分还原形成Si,Ti向铁浴中扩散,Si、Ti在铁浴中的扩散研究结果是: D〓=1.84×10〓exp(-5988.7/T) cm〓/S E〓=49766 J/mol D〓=7.76×10〓exp(-53225.5/T) cm〓/S E〓=442304 J/mol 铁浴式熔融还原熔体对粘土砖,高铝砖,镁砖的侵蚀速度很高,镁碳砖抗侵蚀能力比前几种耐火材料强,但不如铝碳砖;对不含碳耐火材料在熔体中的侵蚀是熔渣中FeO及其它氧化物与耐火材料组分的化学反应形成低熔点物熔蚀进入渣相,产生损毁。
-
Water-quenched samples were prepared by re-melting blast furnace slag and then quenching it at different temperatures. The effects of forming process on the relationship between structure and cementitious reactivity of quenched slag were studied by XRD, DTA, TEM, SEM and EDX techniques in combination with mechanical property and alkali leaching tests.
采用重新熔融水淬的方法制备不同水淬矿渣样品,综合进行净浆强度实验和碱溶出实验研究,借助XRD,DTA,TEM,SEM和EDX等分析手段,研究了矿渣形成过程、形成结构和胶凝性能之间的关系,并在此基础上探讨了矿渣潜在胶凝活性的形成机理。
- 更多网络解释与slag forming相关的网络解释 [注:此内容来源于网络,仅供参考]
-
moldability:造模性
造模设备 molding apparatus | 造模性 moldability | 造渣剂 slag forming constituent
-
alloying constituent:合金剂
造渣剂slag forming constituents | 合金剂alloying constituent | 脱氧剂dioxidizer