rod crack

rod crack的基本解释

-

(钢材或钢丝的)纵裂纹

与rod crack相关的网络例句 [注：此内容来源于网络，仅供参考]

Analyzing the causes of surface crack of GCr15 bearing steel wire with metallurgical microscope, Brinell and Vickers Durometer, the result shows that the surface of wire rod s has no crack, which comes from the course of drawing.

运用金相显微镜、布维氏硬度仪等分析手段，对GCr15轴承钢盘条经拉拔成钢丝后成品表面产生间断裂纹进行分析，结果表明盘条表面无裂纹，成品钢丝的裂纹主要产生于拉拔工艺过程。

Configuration feature: Constant green small tree, gao Keda 8m, bark brown gray, crack, branch is arranged loose, ramose from bottom to top gradually short, establish body tower look, big branch up or bend downward slightly, rod is long and straight, up extend, 4 arris form, close top shows a circle, it is scale leaf completely, scale leaf hands in each other opposite on rod, clingy rod, see 3 impeller are unripe occasionally, scale leaf grows 1.5-3.5mm, pointed or tip acute is blunt, small incurvate, without candle pink, have gland system, gland body is elliptic, be located in a leaf back radical ministry, individual plant of different of male and female, rare with individual plant.

科 属：柏科。圆柏属。形态特征：常绿小乔木，高可达8m，树皮褐灰色，条裂，枝条排列疏松，分枝自下而上渐短，树体塔形，大枝向上或略向下弯曲，小枝长而直，向上伸展，四棱形，近顶端呈圆形，全为鳞叶，鳞叶在小枝上交互对生，紧贴小枝，偶见三叶轮生，鳞叶长1.5-3.5mm，先端锐尖或钝，微内曲，无蜡粉，有腺体，腺体椭圆形，位于叶背基部，雌雄异株，稀同株。

The fracture reasons of high strength PC steel wire are analyzed, it's considered that center segregation, central cavitation, poriness and inclusion are the metallurgical reasons which lead to the facture of PC steel wire and in the rolling process, differential coping quality, microcrack caused by surface defect, abnormal microstructure caused by burnt and improper cooling velocity, the ears on the head of the wire, overlapping of the wire rod itself are the main reasons which lead to the facture of PC steel wire. At the same time, inappropriate pickling, differential phosphorization quality, the bad heat treatment quality, the generation of crack in the improper drawing and transverse crack caused by abnormal laying of the drawing die are also the reasons of the cracking of PC wire.

对高强度PC钢丝断裂原因进行了分析，认为连铸坯的中心偏析、中心缩孔、疏松和夹杂是导致PC钢丝断裂的冶金原因；轧制过程中，较差的修磨质量、表面缺陷导致的微裂纹，过烧以及不适当的冷却速度导致的非正常显微组织，盘条头部的耳子、盘条本身折叠是导致PC钢丝断裂的主要原因；同时，不恰当的酸洗、较差的磷化及热处理质量、不适当拉丝裂纹的产生、拉拔模具安放不正导致的横裂也是PC钢丝断裂的原因。

与rod crack相关的网络解释 [注：此内容来源于网络，仅供参考]

rifting rod：鈎杆

心裂 Rift crack | 鈎杆 Rifting rod | 径断面的 Rift-sawed