So, using magnesia and calcia crucible in VIF respectively, the experiments on deep deoxidation by carbon and the phenomenon of oxygen contamination from crucible materials in the molten steel under some temperature and vacuity and oxygen content of the molten steel were made and it were found that properly low melting temperature and vacuity helped to lighten and even avoid oxygen contamination from crucible material and the refining effect of final oxygen content of 5×10-4% in the molten steel was achieved using calcia crucible with better resistance to thermal shock under higher vacuity.

为此，分别采用MgO炉衬与CaO炉衬，在真空感应炉中对钢液用碳进行深脱氧和炉衬供氧现象实验研究，发现：(1)在适当低的熔炼温度和真空度下，可以减轻甚至避免炉衬热分解向钢液供氧；(2)采用热稳定性优越的CaO炉衬，在较高的真空度下可达到钢液最终全氧含量低于5×10-4%的精炼效果。

By the OM and SEM observation of solidification microstructure, the interfacial reaction between TiAl alloy and Al2O3 crucible was serious, and a large number of α-Al2O3 inclusion formed in the solidification microstructure. The interfacial reaction between TiAl alloy and ZrO2 crucible occurred only on the sample surface, but the crucible was not stable at high temperature and a tack coating was formed, clinging tightly with TiAl alloy. C element in the graphite crucible changed the original solidification path of TiAl alloy, and club-shaped γ-TiAl phases formed.

通过用光学显微镜和扫描电镜对凝固组织观察发现，TiAl合金与氧化铝坩埚之间的界面反应较为严重，在凝固组织中形成了大量氧化铝夹杂；TiAl合金与氧化锆坩埚的界面反应仅发生在试样表面，但该坩埚在高温下不稳定，并在试棒表面形成一层无法剥离的粘结层；石墨坩埚中的C元素改变了原有TiAl合金的凝固路径，生成了棒状的γ-TiAl相。

The furnace shell welded by steel plate and steel,the lini-ng used ultra-light energy from refractory brick masonry, between the shell and lining expansion using silicate fibe-rs and heating insulation powder insulation,high temperat-ure alloy components resistance wire 0Cr25Al5 winding spi-ral formgalvanized-installed in the furnace built around the high alumina brick wire,crucible from Q235 low carbon steel plate from double-sided post-welding,thermocouple inserted from the side hearth furnace,contact crucible,squa-re crucible heat galvanizing EAF matching with automatic t-emperature controlcabinet,at room temperature -500℃ adju-stable within arbitrary and automatic thermostat.

炉壳由钢板和型钢焊接而成，炉衬采用超轻质节能耐火砖砌筑而成，外壳与炉衬之间采用硅酸铝纤维和膨胀保温粉保温加热，元件采用高温合金电阻丝 0Cr25Al5绕制而成螺旋状安装在镀锌炉膛周围的高铝搁丝砖上，坩锅由Q235低碳钢板双面剖焊而成，热电偶从炉体侧面插入炉膛，接触坩锅，方坩锅热镀锌炉配套有自动温度控制柜，在室温-500℃范围内任意可调，并自动恒温。

与crucible相关的网络解释 [注：此内容来源于网络，仅供参考]

crucible：坩埚

大部分数据来自坩埚(crucible)的datasheet,还有一些从网上搜索所得,我是按图表的比例来测量计算出来的,尤其是PDF格式的,因为是矢量图,测量的精确度蛮高的,也通过不同的几份之间进行对比验证,比例值都精确到小数点一位左右BG42和VG10的数据没有找到,

crucible：坩锅

"坩锅"(Crucible)坐落于英国谢菲尔德的谢菲尔德剧院,是谢菲尔德剧院的3个主要场馆之一,另外两个主要场馆叫"学园"(Lyceum)和"演播室"(Studio).

crucible：埚

电子枪式蒸镀机则是利用电子束进行加热,熔融蒸发的金属颗粒全摆在石墨或钨质坩埚(crucible)中. 待金属蒸气压超过临界限度,也开始徐徐蒸着至四周(包含晶圆). 电子枪式蒸镀机可蒸着熔点较高的金属,厚度也比较不受限制.

crucible：炉缸

bosh 炉腹 | crucible 炉缸 | slag tap 放渣口

graphite crucible：石墨坩埚

graphite carbon 石墨碳 | graphite crucible 石墨坩埚 | graphite electrode 石墨电极