The results show that with the increase of hot-pressing temperature, the interior density of composites increases and the pore ratio decreases, and piezoelectric composites hot-pressed at 180～190℃ have the compactest structure and best dielectric and piezoelectric properties.

结果表明，随着热压温度的升高，复合材料内部致密度提高，气孔率降低；当热压温度为180～190℃时，压电复合材料缺陷最少，排列最密实，其介电和压电性也最好。

The result show that the samples are compactest when a-Al2O3/ content is 10wt% at 1450℃, zircon start to decomposes at 1350℃, little mullite are found at 1450℃, there are lots of mullite at 1500℃, apparent poroes become more, bulk density falls.

结果表明，1350℃时硅酸锆已经开始分解，添加a-Al2O3/为10%、温度为1450℃时烧结体最致密，相对密度达到95%，1450℃时已有少量莫来石相形成，1500℃时形成较多莫来石相，气孔增多，体积密度降低。